CarSIK-GD

Ceramics > Kiln Furniture > Batts, Plate-Setters and Lavi-Setter > CarSIK-GD

CarSIK-GD

Bulk density (g/cm³)
3.15

Apparent porosity ( Vol. %)
0
Modulus of rupture (MPa)
280
Weibull modulus
10
Compressive strengths (MPa)
1,000
Modulus of elasticity (GPa)
360
Vickers hardness (MPa)
SiC 25,000
Si 9,000

Thermal expansion 20°-1,000°C
Coefficient (1/°C)
4,9 x 10^-6

Thermal conductivity (W/mK) 100°C
1,200°C

160
24
Specific heat (J/kgK)
RT
1,300°C

600
1,200

Limit of application (°C)
[Melting point silicon (°C)]

1,500
[1,380]
Chemical composition (wt.%)
SiC
free Si

92
7

The values quoted were determined on test specimens and cannot generally be applied to all shapes.

Picture:
Microstructure CarSIK-GD
Dark phase = SiC
Light phase = free Si

	Schunk Ingenieurkeramik GmbH

CarSIK-GD

Bulk density (g/cm3)

3.15

Apparent porosity ( Vol. %)

0

Modulus of rupture (MPa)

280

Weibull modulus

10

Compressive strengths (MPa)

1,000

Modulus of elasticity (GPa)

360

Vickers hardness (MPa)

SiC 25,000 Si 9,000

Thermal expansion 20°-1,000°C Coefficient (1/°C)

4,9 x 10-6

Thermal conductivity (W/mK) 100°C 1,200°C

160 24

Specific heat (J/kgK) RT 1,300°C

600 1,200

Limit of application (°C) [Melting point silicon (°C)]

1,500 [1,380]

Chemical composition (wt.%) SiC free Si

92 7

Bulk density (g/cm³)

SiC 25,000
Si 9,000

Thermal expansion 20°-1,000°C
Coefficient (1/°C)

4,9 x 10^-6

Thermal conductivity (W/mK) 100°C
1,200°C

160
24

Specific heat (J/kgK)
RT
1,300°C

600
1,200

Limit of application (°C)
[Melting point silicon (°C)]

1,500
[1,380]

Chemical composition (wt.%)
SiC
free Si

92
7